anti-corrosion high-quality galvanized steel wire
Galvanized steel wireis made of high-quality low-carbon steel Wire Rod, and refined through multiple processes such as drawing forming, pickling, annealing, galvanizing and cooling. According to the different galvanizing processes, galvanized steel wire can be divided into hot-dipgalvanized steel wire and cold-dip galvanized steel wire (electro-galvanized steel wire). With its excellent toughness, elasticity and anti-corrosion properties, galvanized steel wire is widely used in many fields.
| Galvanized steel wire | |||||
| Diameter （mm） | Tolerance (mm) | Tensile Strength No Less Than (MPA) | Torsion Test No less Than (times) | Bend Times No Less Than (times) | Zinc Coating Mass No Less Than (g/m2) |
| 0.45 | +/-0.01 | 1770 | 28 | 5 | 5 |
| 0.5 | +/-0.01 | 1770 | 28 | 5 | 5 |
| 0.6 | +/-0.01 | 1770 | 28 | 9 | 5 |
| 0.7 | +/-0.01 | 1670 | 28 | 7 | 10 |
| 0.8 | +/-0.01 | 1670 | 28 | 13 | 10 |
| 0.9 | +/-0.02 | 1570 | 28 | 11 | 15 |
| 1 | +/-0.02 | 1470 | 27 | 9 | 20 |
| 1.2 | +/-0.02 | 1470 | 27 | 15 | 20 |
| 1.3 | +/-0.02 | 1370 | 27 | 13 | 20 |
| 1.4 | +/-0.02 | 1370 | 27 | 11 | 20 |
| 1.6 | +/-0.03 | 1370 | 27 | 13 | 20 |
| 1.8 | +/-0.03 | 1370 | 27 | 11 | 30 |
| 2 | +/-0.03 | 1270 | 25 | 10 | 30 |
| 2.4 | +/-0.03 | 1270 | 25 | 11 | 30 |
| 2.6 | +/-0.03 | 1270 | 25 | 10 | 35 |
| 2.77 | +/-0.03 | 1270 | 25 | 9 | 35 |
The production process of galvanized steel wire includes the following key steps:Drawing forming: Drawing high-quality mild steel wire rods to the required diameter.Pickling: Remove rust and impurities from the surface of the steel wire.Annealing: Slow cooling after heating to improve the ductility and toughness of the steel wire.Galvanizing: Through the hot-dip galvanizing or cold-dip galvanizing process, a zinc layer is formed on the surface of the steel wire.Hot-dip galvanizing: The steel wire is immersed in molten zinc to form a thicker zinc layer with stronger protective properties.Cold galvanizing: galvanizing the surface of the steel wire through the electrolysis process, and the zinc layer is thinner.Cooling: Cools the cured zinc layer to ensure that it adheres firmly.
Features:High toughness: It has good elastic and tensile strength, which is suitable for high-strength scenarios.Strong corrosion resistance: the thickness of the zinc layer can reach 300 g/m², which effectively prolongs the service life.Wide range of sizes: Diameters range from 0.2 mm to 6 mm to meet different needs.Cost-effective: reduce maintenance and replacement costs, cost-effective.
Application range of hot-dip galvanized steel wire
Hot-dip galvanized steel wire is particularly good in harsh environments due to its thicker zinc layer and is widely used in the following fields:
Industrial field: chemical equipment, petroleum processing, marine exploration, metal structures, power transmission, shipbuilding, etc.Construction works: scaffolding, bridge cables, highway guardrails, etc.Agricultural production: irrigation systems, greenhouse construction, livestock fencing, etc.Infrastructure: water pipes, gas pipes, electrical pipes, etc.Other areas: handmade, mesh weaving, bundling materials, etc.
With its excellent toughness, elasticity and anti-corrosion properties, galvanized steel wire has become an indispensable material in construction, agriculture, industry and other fields. Whether hot-dip galvanizing or cold-dip galvanizing, galvanized steel wire provides users with reliable support and long-term durability. Choosing the right galvanized steel wire will bring higher efficiency and lower maintenance costs to your project.